Catalytic Activity Evaluation of Molten Salt-Treated Stainless Steel Electrodes for Hydrogen Evolution Reaction in Alkaline Medium

Abstract

The goal of this research is to fabricate a novel type of highly active porous electrode material, based on stainless steel and dedicated to water electrolyzers. The main novelty of the presented work is the innovative application of the molten salts treatment, which allows the design of a highly developed porous structure, which characterizes significantly higher catalytic activity than untreated steel substrates. The equimolar mixture of NaCl and KCl with 3.5 mol% AlF3 was used as the molten salt. The surface modification procedure includes the deposition of an Al layer with application at the potential of −1.8 V and following dissolution at −0.9 V, to create a porous alloy surface. The cathodic polarization measurements of the prepared porous stainless steel electrodes were measured in a 10 mass% KOH solution. Moreover, the amount of hydrogen generated during constant voltage electrolysis with a hydrogen sensor in situ was also measured. The porous stainless steel alloy showed higher current density at lower potentials in the cathodic polarization compared to untreated stainless steel. The cathodic polarization measurements in alkaline solution showed that the porous 304 stainless steel alloy is an excellent cathode material.