Abstract
The chemical structure of a Cu(111) model catalyst during the CO oxidation reaction in the CO+O2 pressure range of 10-300 mTorr at 298-413 K was studied in situ using surface sensitive X-ray photoelectron and adsorption spectroscopy techniques [X-ray photoelectron spectroscopy (XPS) and near edge X-ray adsorption fine structure spectroscopy (NEXAFS)]. For O2:CO partial pressure ratios below 1:3, the surface is covered by chemisorbed O and by a thin (∼1 nm) Cu2O layer, which covers completely the surface for ratios above 1:3 between 333 and 413 K. The Cu2O film increases in thickness and exceeds the escape depth (∼3-4 nm) of the XPS and NEXAFS photoelectrons used for analysis at 413 K. No CuO formation was detected under the reaction conditions used in this work. The main reaction intermediate was found to be CO2(δ-), with a coverage that correlates with the amount of Cu2O, suggesting that this phase is the most active for CO oxidation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.