Abstract
To evaluate the effects of background color, ceramic type and coping thickness on masking ability (ΔE) and translucency parameter (TP) of CAD/CAM lithium disilicate glass-ceramic/monolithic zirconia and, to determine the correlations between coping thickness, TP and ΔE. A total of 120 ceramic specimens (2mm, 1mm and 0.5mm thickness; n=10) of four CAD/CAM ceramics: IPS e.max, IPS ZirCAD, Upcera Li CAD and Upcera TT CAD, were studied. Specimens were tested over nine fabricated backgrounds: A1, A2, A3.5, ND2 and ND7 shade resin-based composites, cobalt-chromium alloy (CC), medium precious alloy (MPA), black (B) and white (W). CIELab values (L*, a* and b*), color difference (ΔE) and translucency parameter (TP) were measured and calculated using a digital spectrophotometer (color i7, X-Rite, Pantone®). Data were analyzed using the Shapiro-Wilk test, one-way ANOVA, three-way ANOVA, independent t-tests and Tukey post-hoc tests (p<0.05). 2mm CAD/CAM ceramics showed ideal color matching (ΔE<2.6) over different backgrounds, except for CC, B and W backgrounds. Monolithic zirconia had lower ΔE values than lithium disilicate glass-ceramics. ΔE and TP values significantly reduced with the increased coping thickness (p<0.05). Regardless of ceramic type and thickness, a strong TP-SD of ΔE correlation was observed. CAD/CAM ceramic restoration color was significantly affected by background color, ceramic type and coping thickness. TP is a promising predictor for appropriate ceramic selection to receive an acceptable CAD/CAM ceramic restoration aesthetic.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.