Abstract
Pt/PbZr0.53Ti0.47O3 (PZT)/LaAlO3 (LAO)/Si and Pt/PbZr0.53Ti0.47O3/La0.85Sr0.15CoO3 (LSCO)/LaAlO3/Si structures for ferroelectric field effect memory applications were fabricated on n-type Si substrate by pulsed laser deposition (PLD). The Auger electron spectrometry (AES) analysis shows that a LaAlO3 buffer layer can effectively prevent Si and Ti, Pb interdiffusion between PZT and Si substrate. For both of the structure, the current density–voltage measurement shows a typical leakage current density of about 10−7A/cm2 at 8V applied voltage. Furthermore, it has been demonstrated that the PbZr0.53Ti0.47O3/LaAlO3/Si structures and Pt/PbZr0.53Ti0.47O3/La0.85Sr0.15CoO3/LaAlO3/Si structures exhibit ferroelectric switching properties, showing a memory window as large as 2 and 2.9V, respectively, under a ramp rate of 200mV/s from −6 to +6V driving voltage at 1MHz. It is believed that the La0.85Sr0.15CoO3 buffer layer deposited on LaAlO3 layer can improve the crystalline properties of PZT films, and then result in lager polarization of PZT and lager memory windows for Pt/PbZr0.53Ti0.47O3/La0.85Sr0.15CoO3/LaAlO3/Si structures.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.