Abstract
The crystal structures of Nb3Te4 and InxNb3Te4 [x = 0.539 (4)] are reported for a series of pressures between 0 and 40 GPa. Both compounds crystallize in space group P6(3)/m with a = b = 10.671 and c = 3.6468 A for Nb3Te4, and a = b = 10.677 and c = 3.6566 A for InxNb3Te4 at ambient conditions. Phase transitions were not observed. High-pressure X-ray powder diffraction was measured using a diamond anvil cell and synchrotron radiation. Full Rietveld refinements provided the values of the lattice parameters and the values of the atomic coordinates at each pressure. The bulk modulus is found as K(0) = 70 (5) GPa for Nb3Te4 and as K(0) = 73 (4) GPa for InxNb3Te4. The analysis of the pressure dependences of the detailed crystal structures shows that the compression along c involves the folding up of the quasi-one-dimensional zigzag chains of Nb. The compression perpendicular to c is entirely due to the reduction of the diameter of the channels. The presence of intercalated In atoms is found to have hardly any influence on the compression behaviour up to 40 GPa.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Acta crystallographica. Section B, Structural science
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.