Abstract
Co-base superalloys are commonly used for vanes and parts of the combustion chamber in gas turbine engines. The Co-base superalloys are primarily solid solution strengthened and have good resistance to hot corrosion, creep, and thermal fatigue. In particular, Co-base alloy X-40 was used to fabricate the first stage NGV airfoils of T56 series engines; inspections after service have revealed that X-40 airfoils suffered from severe thermal fatigue damages. In this study, a new braze repair scheme is proposed; in which Ni-base alloys are used to repair the X-40 substrate in both narrow and wide gap configurations. Metallographic examination, X-ray mapping, and energy dispersive spectroscopy semiquantitative compositional analyses were carried out to study the microstructures in the braze joint in the as-brazed condition and after thermal exposure at 950°C. The results obtained so far suggest the formation of Cr-rich borides, eutectic phases, and various carbides in the joint. No TCP phases were found in the brazed joint and base metals adjacent to the joint. The high carbon content in the alloy X-40 may have played an important role in preventing the formation of TCP phases during brazing and subsequent thermal exposure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.