Abstract
In this work, TiO2/ZrO2 bilayer thin film was prepared on fluorine doped tin oxide (FTO)/glass substrates by using a simple and low-cost chemical solution deposition method. Reproducible bipolar resistive switching (RS) characteristics in Au/TiO2/ZrO2/FTO/glass devices are reported in this work. TiO2/ZrO2 bilayer thin films prepared in this work shows reversible bipolar resistive switching and unidirectional conduction performances under applying voltage and these special performances of TiO2/ZrO2 bilayer thin films was first reported. Obvious resistive switching performance can be observed after setting a compliance current, the ratio of high/low resistance reached about 100 at a read voltage of +0.1V and −0.1V and the RS properties showed no obvious degradation after 100 successive cycles tests. The resistive switching characteristics of Au/TiO2/ZrO2/FTO/glass device can be explained by electron trapping/detrapping related with the vacancy oxygen defects in TiO2/ZrO2 bilayer thin film layer. According to slope fitting, the main conduction mechanisms of the sample are Ohmic and Space charge limited current mechanism.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.