Abstract
Near-stoichiometric Bi1.5Zn1.0Nb1.5O7 (BZN) thin films were prepared on Pt/TiO2/SiO2/Si (100) substrates at 400 °C under an oxygen pressure of 10 Pa by using pulsed laser deposition process. The as-deposited BZN thin films were post-annealed at 700 °C for 30 min in situ vacuum chamber (in situ) and in oxygen ambient oven (ex situ). The crystallinity, microstructure and electrical properties of BZN thin films were investigated. The X-ray diffractometer results indicate that BZN thin films deposited at 400 °C are amorphous in nature and the post-annealed thin films exhibit a cubic pyrochlore structure. The as-deposited BZN thin films show permittivity of 68 and loss tangent of 0.0011 at 10 kHz, respectively. After a post-annealing at 700 °C for 30 min, the dielectric properties of thin films are significantly improved. Permittivity and loss tangent of the in situ annealed films are 127 and 0.005 at 10 kHz, respectively. And the films post-annealed in O2 oven show the largest permittivity of 170 and tangent of 0.006. The improved dielectric properties can attribute to the crystallization of thin films. BZN thin films deposited at low temperature and crystallized at high temperature show the dielectric tunability without an electric breakdown to the maximum measurement bias voltage. And BZN thin films also show the excellent leakage current properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.