Abstract
Silicon carbide is well-known as a high quality wide-band gap semiconductor for use in electronic and optoelectronic applications at high powers, temperatures and radiation environments due to its high breakdown field, wide bandgap, radiation hardness and thermal conductivity. Due to its relatively low lattice mismatch with GaN and AlN and its high thermal conductivity SiC also serves as a high quality, semi-insulating substrate for use in III-N growth for high frequency electronics and optoelectronic devices. Over the past 20 years, dramatic progress in materials and device quality have been realized leading to extremely low-defect density substrates and epilayers. During this same period, significant effort has also been focused on the field of metal-based plasmonics and its applications in enhanced spectroscopy, light emitters, waveguides, and absorbers for photodetectors. However, while metal-based plasmonic systems have attracted attention for their ability to achieve sub-diffraction confinement with large concentrations of electromagnetic fields at optical frequencies, many potentially exciting applications are severely limited by the inherent optical losses caused by the high carrier densities within metals.It has been shown previously that an alternative to plasmonic metals in the mid-infrared-THz spectral ranges are polar dielectrics such as silicon carbide, whereby such large, sub-diffraction limited, localized electromagnetic fields can be sustained through the optical stimulation of plasmon-like surface phonon polaritons (SPhPs). Unlike plasmons, these SPhP modes are due to atomic displacements in polar semiconductors, and thus do not require free carriers to interact with the electromagnetic radiation. Because of this, SPhPs exhibit exceptionally low optical losses. Initial investigations into SiC for SPhPs began in the early part of the last decade and proof-of-principle experiments demonstrated that both localized and propagating SPhP modes could be supported. Recently, our group has demonstrated the first fabricated localized SPhP nano-resonators. The nanostructure arrays are composed of SiC nanoresonators having geometries that are 10 to 40 times smaller than the resonant wavelengths, which occur in the 10.3-12.5 um spectral range. The structures used varied in height from 150-1500 nm-tall nanopillars fabricated from semi-insulating 6H- and 4H-SiC and had diameters ranging from 150-1000 nm and interpillar separations between 20-10,000 nm. The low optical losses resulted in exceptionally narrow resonance linewidths of 3-24 cm-1, corresponding to quality factors in the 40-300 range, which is almost an order of magnitude greater than what is possible with silver (Q<40). Coupled with theoretical simulations of the electromagnetic fields, we have achieved an understanding of the local electromagnetic field distributions and intensities at such extreme confinement as a function of nanostructure size and interpillar separation. This allows us to identify the optical modes involved in the resonances and their optical selection rules. Our work shows that extremely small, high-quality, optical resonators are possible when we use SPhPs instead of surface plasmons in metamaterial designs in the IR. Unlike metals that are limited to the UV-visible, a larger wavelength range is possible with these materials as the phonon modes in polar semiconductors depend on the masses of the constituent atoms and their bond strength.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.