Abstract
The preparation of LaCuOS1−xSex solid solutions (x=0.0, 0.25, 0.5, 0.75, and 1.0) was attempted to control their energy gap and band edge emission energy. X-ray diffraction analysis revealed that the lattice constant of LaCuOS1−xSex increased linearly with increasing x, indicating the formation of a complete solid solution in the LaCuOS–LaCuOSe system. The energy gap estimated from the diffuse reflectance spectra varied continuously from ∼3.1 eV for x=0 to ∼2.8 eV for x=1. The sharp emission near the absorption edge was observed in all samples at room temperature under ultraviolet light irradiation. p-type electrical conduction in these materials was confirmed by Seebeck measurements, and the conductivity was enhanced by substitution of Sr for La. These results demonstrated that the formation of the solid solutions enabled band gap engineering in LaCuOS1−xSex oxychalcogenides keeping their band edge emission feature and p-type conductivity.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call