Band gap and polarizability of boro-tellurite glass: Influence of erbium ions

Abstract

Understanding the influence of rare earth ions in improving the structural and optical properties of inorganic glasses are the key issues. Er3+-doped zinc boro-tellurite glasses with composition 30B2O3–10ZnO–(60−x) TeO2–xEr2O3 are prepared (x=0, 0.5, 1, 1.5 and 2mol%) using melt quenching technique. The physical and optical characterizations are measured by density and UV–Vis–IR absorption spectroscopy. The color of the glass changed from light yellow to deep pink due to the introduction of Er3+ ions. The maximum density is found to be ∼4.73gcm−3 for 1mol% of Er3+ doping. The variations in the polarizability (6.7–6.8cm3) and the molar volume (27.987–28.827cm3mol−1) with dopant concentration are ascribed to the formation of non-bridging oxygen. This observation is consistent with the alteration of number of bonds per unit volume. The direct and indirect optical band gaps are increased while the phonon cut-off wavelength and Urbach energy decreased with the increase of erbium content. A high density and wide transparency range in VIS–IR area are achieved. Our results on high refractive index (∼2.416) and polarizability suggest that these glasses are potential for photonics, solid state lasers and communications devices.