Abstract
A systematic study of the most significant parameters of the ion-assisted deposited silicon dioxide films is carried out using the classical molecular dynamics method. The energy of the deposited silicon and oxygen atoms corresponds to the thermal evaporation of the target; the energy of the assisting oxygen ions is 100 eV. It is found that an increase in the flow of assisting ions to approximately 10% of the flow of deposited atoms leads to an increase in density and refractive index by 0.5 g/cm3 and 0.1, respectively. A further increase in the flux of assisting ions slightly affects the film density and density profile. The concentration of point defects, which affect the optical properties of the films, and stressed structural rings with two or three silicon atoms noticeably decrease with an increase in the flux of assisting ions. The film growth rate somewhat decreases with an increase in the assisting ions flux. The dependence of the surface roughness on the assisting ions flux is investigated. The anisotropy of the deposited films, due to the difference in the directions of motion of the deposited atoms and assisting ions, is estimated using the effective medium approach.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.