Atomic Layer Deposition of Silicon Nitride from Bis(tertiary-butyl-amino)silane and N2 Plasma Studied by in Situ Gas Phase and Surface Infrared Spectroscopy

Abstract

The atomic layer deposition process (ALD) of silicon nitride (SiNx), employing bis(tertiary-butyl-amino)silane (SiH2(NHtBu)2, BTBAS) and N2 plasma, was investigated by means of Fourier transform infrared (FT-IR) spectroscopy. In situ gas phase, film, and surface infrared measurements have been performed during different stages of the ALD process. From gas phase IR measurements it can be concluded that tert-butylamine is the main reaction product released during precursor exposure. Infrared measurements performed on the deposited SiNx films revealed the incorporation of C in the form of CN and SiC, where more C is incorporated at a deposition temperature of 85 °C compared to 155 or 275 °C. Surface IR measurements, employing a four-axes sample manipulator, showed the formation of SiH- and NH-groups on the surface and revealed that most of the H is incorporated during the precursor exposure step. Furthermore, after the N2 plasma step a vibrational mode around 2090 cm–1 was observed. This mode could be attrib...