Abstract

Intergranular corrosion causes a significant loss of compressive strength in highly porous TiO2 foams. In this study, the resistance of conformal atomic layer deposited (ALD) coatings against intergranular corrosion has been investigated. ALD coated TiO2 foams maintained 107%±20% and 94%±10% of their initial compressive strength for films deposited at 150°C and 250°C, respectively. After an immersion period of 28 days in 1mM HCl, amorphous films showed greater potential in corrosion protection of polycrystalline TiO2 foams. However, anatase coatings with sufficient protection may be more beneficial for cell-material interactions.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.