Atomic layer deposited Ta2O5 gate insulation for enhancing breakdown voltage of AlN/GaN high electron mobility transistors

Abstract

AlN/GaN heterostructures with a 3.5 nm AlN cap have been grown by molecular beam epitaxy followed by a 6 nm thick atomic layer deposited Ta2O5 film. Transistors fabricated with 150 nm length gates showed drain current density of 1.37 A/mm, transconductance of 315 mS/mm, and sustained drain-source biases up to 96 V while in the off-state before destructive breakdown as a result of the Ta2O5 gate insulator. Terman’s method has been modified for the multijunction capacitor and allowed the measurement of interface state density (∼1013 cm−2 eV−1). Small-signal frequency performance of 75 and 115 GHz was obtained for ft and fmax, respectively.