Assessment of the catalytic and biological potential of yttrium and samarium-modified copper ferrite nanomaterials

Abstract

The present study reports the preparation of crystalline and nanosized copper ferrite (CuFe2O4), Y3+ substituted CuFe2O4 (CuFe1.95Y0.05O4), and Sm3+ substituted CuFe2O4 (CuFe1.95Sm0.05O4) using a simple co-precipitation method. The XRD analysis confirmed the formation of the cubic spinel phase, while XPS studies validated the presence of Cu and Fe in 2+ and 3+ oxidation states respectively. Transmission electron microscopy (TEM) analysis revealed the nanoparticles with a diameter in the range of 10–60 nm. The introduction of fractional amounts of Y3+ and Sm3+ ions in the CuFe2O4 lattice enhanced the reduction of 4-nitrophenol, attributed to decreased particle size facilitating the reduction process. In the case of antimicrobial activity, Candida albican was found to be maximally sensitive to CuFe2O4 and CuFe1.95Y0.05O4, while Pseudomonas aeruginosa was inhibited by CuFe1.95Sm0.05O4. Moreover, a maximum of 61.9 ± 1.91 % anti-Pseudomonas biofilm activity and 75.7 ± 1.28 % DPPH radical scavenging activity was observed for CuFe1.95Y0.05O4 at 200 μg/ml concentration. The improvement in biological activities was attributed to the reduced particle size, crystal structure modification, and increased stability of the CuFe2O4 lattice with substitution. The enhancement in catalytic and biological performance highlighted the effectiveness of minimal Y3+ and Sm3+ concentrations in modulating the properties of CuFe2O4 nanomaterials.