Abstract
Polycrystalline CoFe2O4 thin films are deposited onto the quartz substrates by spray pyrolysis technique. Rietveld refinement analysis confirmed the films are polycrystalline in nature with spinel cubic crystal structure. Rietveld refinement analysis was employed to estimate the cation distribution in spinel lattice sites. Surface micrographs shows the granular morphology with average grain size decreases with increase in solution concentration. The presence of two characteristic absorption bands around 579 and 391cm−1 in the FTIR study confirms the formation of single phase CoFe2O4. Vibrating sample magnetometer measurement confirmed the predominant ferrimagnetic nature of thin films which confirms the maximum saturation magnetization with moderate coercivity was useful for making effective gas sensor. The gas response towards different operating temperatures, gas concentrations and solution concentrations was systematically studied. The films show the maximum gas response 70% at 0.1M solution concentration at 150°C operating temperature. The films are well selective towards NO2 as compared with other test gases with good reproducibility.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.