Abstract
The effect of the gas-nitriding thermochemical treatment on the cavitation erosion resistance of a Cr-Ni-Mo alloy is analyzed using a piezoceramic vibrating equipment and following the ASTM G32-2010 standard. The evaluation of the cavitation erosion behavior was made based on the analysis of the mean depth of erosion (MDE) and mean depth of erosion rate (MDER), for samples subjected to the cavitation erosion for different times. The surface topography and the structural changes in the marginal layer were analyzed through optical and scanning electron microscopy. Following nitriding the cavitation erosion resistance was about 9.6 times higher compared to the annealed state and about 8.2 times higher compared to the hardened and tempered state.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.