Abstract
We demonstrate the synthesis of near-IR-emitting zinc blende CdTe/CdS tetrahedral-shaped nanocrystals with a magic-sized (approximately 0.8 nm radius) CdTe core and a thick CdS shell (up to 5 nm). These high-quality water-soluble nanocrystals were obtained by a simple but reliable aqueous method at low temperature. During the growth of the shell over the magic core, the core/shell nanocrystals change from type I to type II, as revealed by their enormous photoluminescence (PL) emission peak shift (from 480 to 820 nm) and significant increase in PL lifetime (from approximately 1 to approximately 245 ns). These thick-shell nanocrystals have a high PL quantum yield, high photostability, compact size (hydrodynamic diameter less than 11.0 nm), and reduced blinking behavior. The magic-core/thick-shell nanocrystals may represent an important step toward the synthesis and application of next-generation colloidal nanocrystals from solar cell conversion to intracellular imaging.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.