Apoptotic effects of biodentine, calcium-enriched mixture (CEM) cement, ferric sulfate, and mineral trioxide aggregate (MTA) on human mesenchymal stem cells isolated from the human pulp of exfoliated deciduous teeth.

Abstract

Preservation of primary teeth in children is highly important. Pulpotomy is a commonly performed treatment procedure for primary teeth with extensive caries. Thus, biocompatibility of pulpotomy agents is highly important. Biodentine, calcium enriched mixture (CEM) cement, ferric sulfate, and mineral trioxide aggregate (MTA) Angelus are commonly used for this purpose. Thus, this study aimed to assess the apoptotic effects of Biodentine, CEM cement, ferric sulfate, and MTA on stem cells isolated from the human pulp of exfoliated deciduous teeth. In this in-vitro, experimental study, stem cells isolated from the human pulp of exfoliated deciduous teeth were exposed to three different concentrations of Biodentine, CEM cement, ferric sulfate, and MTA for different time periods. The cytotoxicity of the materials was evaluated by flow cytometry using the annexin propidium iodide (PI) kit. Data were analyzed by ANOVA and Tukey's test at P<0.05 level of significance. All four tested materials induced significantly greater apoptosis compared with the control group. The difference in cell apoptosis caused by the first concentration of ferric sulfate and MTA was not significant at 24 hours. In other comparisons, the cytotoxicity of ferric sulfate was significantly lower than that of other materials. Biodentine showed higher cytotoxicity than MTA at first; but this difference faded over time. The cytotoxicity of CEM cement was comparable to that of MTA. The highest cell viability was noted at 24 hours in presence of the minimum concentration of ferric sulfate. The lowest cell viability was noted at 72 hours in presence of the maximum concentration of CEM cement. In comparison with other materials, ferric sulfate showed minimum cytotoxicity; the cytotoxicity of the three cements was comparable. It appears that the concentration of ferric sulfate and the composition of cements are responsible for different levels of cytotoxicity.