Antibacterial calcium phosphate cement with human periodontal ligament stem cell‐microbeads to enhance bone regeneration and combat infection

Abstract

Infectious bone defects remain a significant challenge in orthopedics and dentistry. Calcium phosphate cement (CPC) have attracted significant interest in use as local drug delivery system, which with great potential to control release of antibiotics for the treatment of infectious bone defects. Within the current study, a novel antibacterial scaffold of chitosan-reinforced calcium phosphate cement delivering doxycycline hyclate (CPCC + DOX) was developed. Furthermore, the capacity of CPCC + DOX scaffolds for bone regeneration was enhanced by the human periodontal ligament stem cells (hPDLSCs) encapsulated in alginate beads. CPCC + DOX scaffolds were fabricated to contain different concentrations of DOX. Flexural strength of CPCC + DOX ranged from 5.56 ± 0.70 to 6.2 ± 0.72 MPa, which exceeded the reported strength of cancellous bone. Scaffolds exhibited continual DOX release, reaching 80% at 21 days. Scaffold with 5 mg/ml DOX (CPCC + DOX5mg) had a strong antibacterial effect, with a 4-log colony forming unit reduction against S. aureus and P. gingivalis. The proliferation and osteogenic differentiation of hPDLSCs encapsulated in alginate hydrogel microbeads were investigated in culture with CPCC + DOX scaffolds. CPCC + DOX5mg had no negative effect on proliferation of hPDLSCs. Alkaline phosphatase activity, mineral synthesis, and osteogenic gene expressions for CPCC + DOX5mg group were much higher than control group. DOX did not compromise the osteogenic induction. In summary, the novel CPCC + DOX scaffold exhibited excellent mechanical properties and strong antibacterial activity, while supporting the proliferation and osteogenic differentiation of hPDLSCs. The CPCC + DOX + hPDLSCs construct is promising to enhance bone regeneration and combat bone infections in dental, craniofacial, and orthopedic applications.