Abstract
Mn1.4Ga films with high perpendicular magnetic anisotropy and high crystalline quality were grown on MgO substrates with Cr buffer layer using molecular beam epitaxy. The crystalline structure and the surface morphology of the films have been systematically investigated as functions of in-situ annealing temperature (Ta) and film thickness. It is found that the magnetic properties can be largely tuned by adjusting Ta. As Ta increases, both saturation magnetization (Ms) and uniaxial perpendicular magnetic anisotropy constant (Ku) increase to the maximum values of 612 emu/cc and 18 Merg/cc at 300 °C, respectively, and then decrease. The morphology also changes with Ta, showing a minimum roughness of 2.2 Å at Ta = 450 °C. On the other hand, as the thickness increases, Ms and Ku increase while coercivity decreases, which indicates there is a magnetic dead layer with a thickness of about 1.5 nm at the interfaces. The detailed examination on the surface morphology of the films with various thicknesses shows a complicated film growth process, which can be understood from the relaxation mechanism of the interfacial strain.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.