Annealing induced morphological modifications in PTFE films deposited by magnetron sputtering

Abstract

As grown RF magnetron sputtered polytetrafluoroethylene (PTFE) thin films were subjected to vacuum annealing at optimized elevated temperature of 200° C for varying time duration and corresponding surface morphological changes were recorded. The columnar structures appearing after an annealing duration of 2 hours are interesting for fabrication of rough PTFE surfaces towards possible applications in hydrophobicity along with high transmission. Supported by transmission data, the AFM images show a transformation of smooth PTFE surface with less than 2 nm rms roughness to a very rough surface. The results are interpreted in terms of thermal energy induced modifications only at the surface without any change in the original bonding structure on the surface and inside the sample. Preliminary studies indicate that the optimization of roughness and transmission together on such surfaces may lead to high water contact angles.As grown RF magnetron sputtered polytetrafluoroethylene (PTFE) thin films were subjected to vacuum annealing at optimized elevated temperature of 200° C for varying time duration and corresponding surface morphological changes were recorded. The columnar structures appearing after an annealing duration of 2 hours are interesting for fabrication of rough PTFE surfaces towards possible applications in hydrophobicity along with high transmission. Supported by transmission data, the AFM images show a transformation of smooth PTFE surface with less than 2 nm rms roughness to a very rough surface. The results are interpreted in terms of thermal energy induced modifications only at the surface without any change in the original bonding structure on the surface and inside the sample. Preliminary studies indicate that the optimization of roughness and transmission together on such surfaces may lead to high water contact angles.