Annealing Effects on Electrical Properties of Pure and Tin-Doped Indium Oxide Thin Films

Abstract

The annealing effects on the properties of ITO and pure In2O3 thin films have been investigated. The thin films were deposited with various O2 flow ratios to total gas flow by pulsed dc magnetron sputtering. The post-deposition annealing of the thin films was carried out for 30 minutes at various temperatures ranging up to 500 degrees C in air. It was found through the comparison of the carrier density of ITO and In2O3 thin films that the carrier electrons of the ITO thin films came from both of the dopant Sn and oxygen vacancies under the annealing less than 400 degrees C. Therefore, the ITO thin films deposited with lower O2 flow ratio exhibited higher carrier density due to many oxygen vacancies; in consequence, they exhibited lower resistivity at the annealing up to 400 degrees C. On the other hand, the carrier density of ITO thin films was almost identical regardless of O2 flow ratio when they were annealed at 500 degrees C. This fact indicates that most carrier electrons of the ITO thin films were brought by the dopant Sn at the annealing temperature of 500 degrees C. However, the ITO thin films deposited with lower O2 flow ratio exhibited higher Hall mobility; as a result, they showed lower resistivity at the annealing of 500 degrees C. Atomic force microscope, X-ray diffraction and X-ray reflectivity measurements revealed that the ITO thin films deposited with lowe O2 flow ratio exhibited dense structure even after they were annealed at 500 degrees C. Hence, the carrier electrons of the dense ITO thin films deposited with low O2 flow ratio can conduct better, as a result, the ITO thin films exhibited high Hall mobility and low resistivity.