Abstract
(001)-oriented ZnO films on Zn substrates were synthesized by cathodic electrodeposition from an aqueous solution composed only of 0.05 M zinc nitrate at 65 °C. A bound exciton emission band around 3.34 eV along with three longitudinal optical (LO) phonon replicas and an intensive broad emission band around 2.17 eV were observed from the photoluminescence (PL) spectra of ZnO films prepared at more positive potential (− 0.6∼− 0.8 V). When more negative potential (− 1.0∼− 1.4 V) was applied, the ultraviolet emission band disappeared. These results indicate that more positive electrodeposition potential favors the high quality ZnO film growth. The PL spectra of the annealed ZnO films prepared at more positive electrodeposition potentials − 0.6∼− 1.0 V exhibit the ultraviolet emission at 3.35 eV and a negligibly weak emission from defects. Annealing resulted in the enhancement and sharpening of the excitonic emission band and decrease of the deep level emission. The bandgap ( E g) of the ZnO film prepared at − 1.0 V on indium tin oxide (ITO) substrate decreased from 3.56 to 3.29 eV due to the removing of Zn(OH) 2 from the film after annealing.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.