Abstract
Cryogenic interlaminar beam tests in the form of three-point flexure are examined both experimentally and analytically. The use of the short-beam shear test for measuring the interlaminar shear strength of glass-cloth/epoxy laminates at low temperatures is evaluated first. The interlaminar shear tests were carried out with short-beam shear specimens at room temperature, 77 K and 4 K to evaluate the interlaminar shear strength of G-10CR glass-cloth/epoxy laminates. Each specimen was placed on two roller supports that allow lateral motion and a load was applied directly at the center of the specimen. These tests were conducted in accordance with ASTM, 1984, “Standard Test Method for Apparent Interlaminar Shear Strength of Parallel Fiber Composites by Short-Beam Method,” Designation D2344-84. The effects of temperature, specimen width, and span-to-thickness ratio on the apparent interlaminar shear strength are shown graphically. Photomicrographs (scanning electron micrographs, optical micrographs) of actual failure modes were utilized to verify the failure mechanisms. A three-dimensional finite element analysis was also performed to investigate the effects of specimen width and span-to-thickness ratio on the shear stress distribution in the mid-plane. Effective elastic moduli were determined under the assumption of uniform strain inside the representative volume element. The numerical findings are then correlated with the experimental results.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.