Abstract
In this paper, upconversion (UC) luminescence processes in a GeO2-Ga2O3-BaO glass system codoped with 0.7Yb2O3/(0.07-0.7)Tb2O3 (mol.%) and double-clad optical fiber codoped with 0.7Yb2O3/0.7Tb2O3 (mol.%) were investigated. The highest emission intensity (energy transfer efficiency equals 12.92%) was obtained for 0.7Yb2O3/0.7Tb2O3 codoped glass. Comparative analysis showed significant differences in the shape of luminescence of fabricated germanate glass and optical fiber. Due to dominant transition from D45 sublevel the main green UC peak (Tb3+: D45→F57) of fabricated double-clad optical fiber is shifted by 4nm toward longer wavelengths.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.