Abstract
Stainless steel and nickel alloy have high corrosion resistance in high-temperature environments due to the high Cr content present in their chemical composition, being widely used in components of nuclear reactors, petrochemical industries, etc. Through proper processes and procedures, it becomes possible to join these alloys. However, this union can generate detrimental factors in its performance, among them, the residual stresses. In this work, the residual stresses generated by the autogenous GTAW process, due to different interpass temperatures on the weld bead geometry, were analyzed by the Hole-Drilling technique in dissimilar welding joints of stainless steel AISI 316L and Inconel 718 alloy. In addition, the Vickers microhardness measurements were carried out to evaluate the hardness profile in the cross section of the weld bead covering base metal (BM), heat affect zone (HAZ) and weld metal (WM). We found that in the interface region between BM and HAZ of each dissimilar joint metal, residual stresses increased above 300 MPa, while hardness increased above 160 HV.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.