Abstract
The influence of manganese in Zn-Mn and Zn-0.2wt.%Al-Mn bath on the morphology and growth kinetics of the galvanizing coatings has been studied using scanning electron microscopy equipped with energy dispersive spectroscopy. When galvanized in zinc bath, the coating consists mainly h and ζphase. When manganese is added in zinc bath, the morphology of ζ phase changes from fragmental to compact. Manganese favors the formation of the δ phase and inhibits the growth of the ζ phase.When galvanized in Zn-0.2wt.%Al bath, the coating consists only δ and h phase. With the addition of manganese in Zn-0.2wt.%Al bath, the morphology of δ phase changes from fragmental to compact The thickness of the Fe-Zn intermetallic phase layer in coatings decreases obviously when manganese is added into zinc and Zn-0.2wt.%Al bath, and the thickness increases slowly with the increase of immersion time.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.