Abstract
Analysis of SrTiO<sub>3</sub> ceramics with the doping Cuprum(II) acetate (Cu(CH<sub>3</sub>COO)<sub>2</sub>), the variation in the concentration of doping used 0%; 0,5%; and 1% using the solid state reaction method was successful. The annealing process is carried out starting from room temperature then raised to an annealing temperature of 850 <sup>o</sup>C with a temperature increase of 1,67 <sup>o</sup>C / minute and held constant for 8 hours. Next proceed with the cooling process until it returns to room temperature for 13 hours. Analysis of XRD data using the Cramer-Cohen method yielded a lattice parameter of 3,909 Å; 3,906 Å; and 3,905 Å, a cubic crystal structure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.