Abstract
ABSTRACTWe have measured stress variations with temperature as a function of film thickness and a given grain size in pure Al and AI-0.5%Cu films on Si substrates. The variation in thickness for a given grain size is brought about by using the same film and the repeated controlled growth and dissolution of a barrier anodic oxide which can be grown uniformly on the film. Stress measurements were made as a function of temperature by measuring wafer curvature after successively removing each 0. Iμm of Al film. The components of strengthening due to the film thickness and the presence of grain boundaries were separated by assuming that the flow stress of the film is simply the sum of these two components. The observations are consistent with results obtained using lascr-rcflowed films in an earlier work. The variations of these two components with temperature, and under tension and compression is discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.