Abstract
ABSTRACT The microstructure just below the fracture surface in hydrogen-charged stable austenitic SUS 316L stainless steel, which was subjected to a low strain rate tensile test at −70°C, was studied by a combination of the focused-ion-beam method and transmission electron microscopy. An amorphous region with a chemical composition almost identical to that of the polycrystalline region was found under the lath-like structure on the fracture surface, although no deterioration of tensile properties by hydrogen appeared. In the amorphous region, band-like regions with wavy contrasts were observed, which were often accompanied by cracks at the boundaries. The presence of the amorphous region with band-like regions implies that amorphization occurred due to high-density vacancies accompanied by agglomerations of excess vacancies in the hydrogen-charged SUS 316L stainless steel that was tensile-tested at low temperatures.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.