Abstract

To process an alumina-toughened zirconia (ATZ) nanocomposite and to characterize its crystalline phases, microstructure, residual stress, mechanical and optical properties before and after two different artificial aging methodologies. Disc-shaped specimens were obtained through uniaxial pressing of a commercial ATZ powder comprised of 80%ZrO2 / 20%Al2O3, with a particle size of 50nm and 150nm, respectively. Sintering was performed at 1500ºC for 2h. Groups were established according to the aging protocol as immediate (ATZ-I) and aged either in autoclave (ATZ-A) or hydrothermal reactor (ATZ-R) at 134 ºC for 20h at 2.2bar. Crystalline phases and microstructure were assessed by X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. Residual stress was evaluated by Raman spectroscopy. Contrast Ratio (CR) and Translucency Parameter (TP) were calculated to characterize optical properties. Mechanical properties were analyzed through Vickers microhardness, fracture toughness, and biaxial flexural strength test. XRD spectra of both aging protocols revealed the presence of monoclinic zirconia (20-31%), where higher phase transformation was observed after aging in hydrothermal reactor. Optical properties evaluation demonstrated high opacity (CR: 0.99) and masking ability (TP: 0.26), with no significant differences after aging. Raman spectroscopy evidenced the presence of residual compressive stresses in the aged groups, being significantly higher for ATZ-R (-215.2MPa). As-sintered specimens revealed hardness of ∼12.3GPa and fracture toughness of ∼1.9MPa.m1/2. Characteristic strength was 740MPa for ATZ-I, 804MPa for ATZ-A, and 879MPa for ATZ-R, with significant differences between groups. Weibull modulus ranged from 16.5 to 18.8. All groups demonstrated high reliability up to 500MPa stress missions (99-100%), with no significant differences after aging. The experimental ATZ nanocomposite presented high opacity and a high Weibull modulus. While aging created internal compressive stress responsible for an increase in characteristic strength, the nanocomposite was susceptible to hydrothermal degradation. Further studies are required to evaluate its degradation kinetics at low temperatures.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call