Abstract
A break of wiring by stress-migration becomes a problem with an integrated circuit such as LSI. The present study investigates residual stress in SiO 2/Cu/TiN film deposited on glass substrates. A TiN layer, as an undercoat, was first deposited on the substrate by arc ion plating and then Cu and SiO 2 layers were deposited by plasma coating. The crystal structure and the residual stress in the deposited multi-layer film were investigated using in-lab. X-ray equipment and a synchrotron radiation device that emits ultra-high-intensity X-rays. It was found that the SiO 2 film was amorphous and both the Cu and TiN films had a strong {1 1 1} orientation. The Cu and TiN layers in the multi thick (Cu and TiN:1.0 μm)-layer film and multi thin (0.1 μm)-layer film exhibited tensile residual stresses. Both tensile residual stresses in the multi thin-layer film are larger than the multi thick-layer film. After annealing at 400 °C, these tensile residual stresses in both the films increased with increasing the annealing temperature. Surface swelling formations, such as bubbles were observed in the multi thick-layer film. However, in the case of the multi thin-layer films, there was no change in the surface morphology following heat-treatment.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.