Abstract
Twin-roll cast (TRC) AZ31 alloy (Mg–3 wt.% Al–1 wt.% Zn) was subjected to annealing heat treatment at 420 °C which resulted in an important change in the original strong basal texture. It was observed that the unique TRC structure, which is a combination of both cast and deformed structures, is responsible for this texture alteration upon annealing. The change in crystallographic orientation is attributed to the particle-stimulated nucleation of new grains with random orientations.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.