Twin-roll cast (TRC) AZ31 alloy (Mg-3wt.%Al-1wt.%Zn) was subjected to heat treatment at 420 °C. As a result, the intensity of the original basal texture was reduced considerably. Crystallographic orientation analysis revealed that such a change in the texture is due to particle-stimulated nucleation of new grains with random orientations. The tensile test results indicate that annealing slightly increases ultimate tensile strength (UTS), however, dramatically improves the elongation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.