Abstract
Alignment control of three dimensional (3D) SiGe nanodot arrangements is investigated using a reduced pressure chemical vapor deposition system. Several cycles of SiGe layers with 30% Ge content and Si spacers are deposited by SiH4-GeH4 at 550 °C and SiH4 or SiH2Cl2 at 700 °C, respectively, to form a 3D SiGe nanodot structure. By using SiH4 as a precursor for the Si spacer deposition, SiGe nanodots are aligned at staggered positions resulting in a body-centered tetragonal (BCT) structure, because a checkerboard mesa structured Si surface is formed and the next SiGe nanodot formation occurs at the concave region to reduce surface energy. On the other hand, after planarizing the Si surface with checkerboard structure by chemical mechanical polishing (CMP), the new SiGe nanodot formation occurs directly above the embedded SiGe nanodot located nearest to the Si surface (dot-on-dot). The driving force seems to be local tensile strain formed at the Si surface above the embedded SiGe nanodot. By using SiH2Cl2 as precursor for the Si spacer deposition, a smooth Si surface can be realized on BCT SiGe nanodot structures without CMP process resulting in a vertically aligned SiGe nanodot formation. The local tensile strain formation in Si above SiGe nanodots is confirmed by nano beam diffraction analysis.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.