Abstract
The outstanding photoelectric properties of perovskites demonstrate extreme promise for application in X-ray detection. However, the soft lattice of the perovskite results in severe ionic migration for three-dimensional materials, limiting the operation stability of perovskite X-ray detectors. Although ligand-decorated nanocrystals (NCs) exhibit significantly higher stability than three-dimensional perovskites, defects remaining on the interface of NCs could still trigger halide migration under a high bias due to the incomplete ligand decoration. Furthermore, it is still challenging to realize sufficient thickness of absorption layers based on NCs for X-ray detectors through traditional methods. Herein, we develop a centimeter-size and millimeter-thick wafer based on CsPbBr3 NCs through isostatic pressing for X-ray detectors, in which the interfacial defects of NCs are remedied by CsPb2Br5 during aging of wafer in ambient humidity. The wafer shows outstanding sensitivity (200 μC Gyair-1 cm-2) and ultralow dark current drift (1.78 × 10-8 nA cm-1 s-1 V-1 @ 400 V cm-1). Moreover, it shows storage stability with negligible performance degradation for 60 days in ambient humidity. Thus, aging perovskite NC wafers for X-ray detection holds huge potential for next-generation X-ray imaging plates.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.