Abstract
In order to investigate the effects of different crosslinking agents on physicochemical properties and adsorption properties of porous starch. Native corn starch was hydrolyzed by maltase and crosslinked with different crosslinking agents. Sodium trimetaphosphate crosslinked porous starch (STMP-MPS), malic acid cross-linked porous starch (MA-MPS) and citric acid cross-linked porous starch (CA-MPS) were prepared. After crosslinking, MA-MPS and CA-MPS showed a new CO stretching absorption peak at 1738 cm−1, and the crosslinking degree was much higher than that of STMP-MPS. The surface area of MA-MPS was 36 % higher than that of STMP-MPS. Compared with the average pore size of 12.43 nm of STMP-MPS, CA-MPS (14.02 nm) and MA-MPS (14.79 nm) were increased more significantly. The degradation temperature of MA-MPS and CA-MPS was increased by the introduction of ester bond, which indicates that the organic acid cross-linking strengthens the starch granules and hence more energy is required for disruption. Compared with STMP-MPS, the water absorption of MA-MPS and CA-MPS increased by 64 % and 32 %, respectively. Furthermore, the adsorption capacity of MA-MPS to essential oil was the strongest, about 4 times that of STMP-MPS. Overall, it is feasible to modify porous starch by crosslinking reaction to improve its heat resistance and adsorption properties.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call