Abstract
The time-transition curve of open circuit potential (Eoc) during the single zincating process of aluminium alloy 7075 (AA7075) was recorded. Then, a suitable single zincating duration was selected from the Eoc slope, in order to get the optimum zincating duration. The evolution of surface morphology and composition of AA7075 substrate at various single zincating durations were characterized by scanning electron microscopy (SEM) and energy dispersive analysis of x- rays (EDX). The coating adhesions of single zincated samples produced at various durations were investigated using a scratch tester. SEM results showed that the substrates produced at a longer zincating duration were fully covered by a dense layer of zinc particles. The adhesion of the electrodeposited nickel on single zincated samples produced at longer zincating duration was higher than the conventional single zincating process. This morphology has contributed to the improvement of coating adhesion.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.