Abstract
Novel manufacturing techniques such as additive manufacturing also referred to as 3D printing hold a critical role in the preparation of novel bioactive three-dimensional glass-ceramic scaffolds. The present paper focuses on the use of Ca–Mg silicates microspheres (Ca2MgSi2O7, i.e. 40 mol% CaO, 20% MgO and 40% SiO2) for the fabrication of 3D structures by additive manufacturing. In the first step, the crystallization of the åkermanite system was avoided, by feeding nearly fully crystallized precursor powders prepared by conventional melt quenching into oxygen-methane (O2/CH4) torch, and solid glass microspheres (SGMs) with diameters bellow 63 μm were prepared. In the second step, the crystallization was utilized to control the viscous flow of SGMs during firing of reticulated scaffolds, obtained by digital light processing (DLP) of the SGMs suspended in a photocurable acrylate binder. The spheroidal shape facilitated a high solid content, up to 77 wt% of the SGMs in the suspension. After burn-out of the organic binder, a fast sintering treatment at 950 °C, for 30 min, led to scaffolds preserving the macro-porosity from 3D printing model (diamond cell lattice) but with well densified struts. The crystallization of 3D scaffolds during the sintering process led to 3D structures with adequate strength-to-density ratio.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.