Abstract
AbstractThe occurrence and expansion of fatigue cracks in large wind turbine blades may lead to catastrophic blade failure. Each fatigue phase of a material has been associated with a typical set of acoustic emission (AE) signal frequency components, providing a logical base for establishing a clear connection between AE signals and the fatigue condition of a material. The relevance of efforts to relate recorded AE signals to a material's mechanical behaviour relies heavily on accurate AE signal processing. The main objective of the present study is to establish a direct correlation between the fatigue condition of a material and recorded AE signals. We introduce the blind deconvolution separation (BDS) approach because the result of AE monitoring is usually a convoluted mixture of signals from multiple sources. The method is implemented on data acquired from a fatigue test rig employing a wind turbine blade with an artificial transverse crack seeded in the surface at the base of the blade. Two different sets of fatigue loading were conducted. The convoluted signals are collected from the AE acquisition system, and the weak crack feature is extracted and analysed based on the BDS algorithm. The study reveals that the application of BDS‐based AE signal analysis is an appropriate approach for distinguishing and interpreting the different fatigue damage states of a wind turbine blade. The novel methodology proposed for fatigue crack identification will allow for improved predictive maintenance strategies for the glass‐epoxy blades of wind turbines. The experimental results clearly demonstrate that the AE signals generated by a fatigue crack on a wind turbine blade can be synchronously separated and identified. Characterizing and assessing fatigue conditions by AE monitoring based on BDS can prevent catastrophic failure and the development of secondary defects, as well as reduce unscheduled downtime and costs. The possibility of using AE monitoring to assess the fatigue condition of fibre composite blades is also considered.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Fatigue & Fracture of Engineering Materials & Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.