Abstract
Silver-rich metal powders cold-welded by consolidation have been investigated as possible direct dental filling material. The surface of the silver powder must undergo an acid treatment to remove existing contaminants and prevent formation of new surface contaminants during consolidation. This study was designed to investigate the effect of the acid treatment on the strength of the consolidated alloy, its reactivity with the surrounding tooth structure, and its reactions with certain cavity liners.This study investigated the effects of pH and concentration of fluoboric acid on the flexural strength of silver powder consolidated into rectangular beams in a partial 4 × 4 design. The study also assessed, by visible and scanning electron microscopy, what effect the acid-treated powders had on dentin that had been pre-coated with different cavity liners. Mean flexural strengths for beams consolidated using dental hand instruments were in the range (77.0 ± 9.28) MPa to (166.1 ± 17.6) MPa, where the quoted uncertainties are standard uncertainties (i.e., one standard deviation estimates). ANOVA indicated that fluoboric acid pH was highly significant (p < 0.0001) with lower pH values resulting in higher flexural strength. Concentration alone was not a significant factor for flexural strengths, but there was a significant interaction between concentration and pH (p < 0.0001). Microscopy revealed that the acid-treated silver powder demineralized approximately 2 μm of dentin when used with no liner. The use of copal or polyamide varnishes eliminated most of this demineralization, but the use of a dentin adhesive liner resulted in some dislodgment and breakdown of the adhesive film by the acid.The results of this study indicate that this silver powder when treated with dilute fluoboric acid at a pH of approximately 1.0 can result in a filling material with strength equivalent to currently used conventional amalgam. The demineralization of tooth structure appears to be minimal and can be eliminated with the use of cavity liners.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of research of the National Institute of Standards and Technology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.