Abstract
Abstract Shear plastic deformation in ECAP occurs through the formation, movement and storage of dislocations. The differences which exist between shearing characteristics lead to important implications concerning the optimum processing route. It is known that the effectiveness of cell evolution into an array of high-angle boundaries (HABs) is in the order BC > C > A, or A > BC > C, depending on the two-channel-angle intersection of the ECAP die. In route A, large portions of HABs are continuously and progressively generated, while routes C and BC cause fully redundant deformation at each 2n passes, and each 4n passes, respectively. This study is focused on dislocation generation, storage and recombination during ECAP for routes A, C and BC. Kikuchi bands identified with TEM were used to quantitatively measure the cell and grain boundary misorientation. ECAP was performed on an AA1200 commercially pure aluminium alloy up to e = 8.64. A different hierarchy for HAB generation efficiency was found. Thermal stability was studied by annealing the alloy at 0.5, 0.6, 0.7 TM (where TM is the alloy melting point) for 2 h after the severe plastic deformation. It appeared that, even if route BC involves the fastest microstructure grain refining, route C is likely to be the most stable upon reheating.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call