Abstract
In the investigative study of the Isotropic Graphite IG-110 of Toyo Tanso, the shore hardness test, compressive test, bending test and fracture toughness test were conducted. The compressive test, the bending test and the fracture toughness test were performed by MTS-810. Test velocity of the compressive and the bending test were 0.5mm/min and the fracture toughness test were 0.1mm/min. The results were compared with manufacturer data of Toyo Tanso. Through irradiation test using HANARO research reactor, hardness and strength of nuclear graphite IG-110 was examined. Strength and hardness of irradiated steel is higher than non-irradiated, but nuclear graphite IG-110 declined unlike steel. To search for characteristic change of nuclear graphite IG-110 under the amounts of neutron, a repeat of the experiment was conducted.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.