Abstract
Research was conducted on tailored blank welding between mild steel sheet and Zn-coated steel sheet using CO2 laser beam. The materials used in this study were low carbon steel sheets with a thickness of 1.2 mm and Zn-coated steel sheet with the same thickness and 6.3 μm Zn coating. Experiments were conducted by applying the Taguchi method to obtain optimum conditions for the application of this tailored blank laser welding method in practical manufacturing processes. Optical microscopy, XRD, SEM and TEM analysis were performed to observe the microstructures and to determine the structures of welded zone. In addition, mechanical properties were measured by the microhardness test, tensile test and Erichsen test to evaluate the formability of the welded specimen. There was no trapped Zn in the fusion zone, and the phases of this region consisted of polygonal ferrite, quasi-polygonal ferrite, banitic ferrite and martensite. The elongation value of welded specimen was more than 80% of the value in substrate metal, and the LDH value was more than 90% of the value in substrate metal.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.