Abstract
Fluoroborosilicate glasses of composition 35SiO2-25B2O3-10Na2CO3-15NaF-15CaF2-xNd2O3 (where x = 0.1, 0.5. 1.0, 2.0 mol%) were prepared by melt quenching technique and various physical properties have been calculated. From the absorption spectra J-O Intensity parameters Ωλ (λ = 2, 4, 6) and radiative properties are evaluated by using J-O theory. The high values of Ω2 = 4.213 × 10−20 cm2, Ω4 = 5.345 × 10−20 cm2, Ω6 = 5.526 × 10−20 cm2 suggest that among the prepared glasses 0.5 mol% Nd glass is more asymmetric, more covalent and rigid in nature. The emission spectra were recorded with 808 nm laser as excitation source. The strong NIR emissions were observed at 876 nm, 1056 nm, 1328 nm corresponding to the transitions 4F3/2 → 4I9/2, 4F3/2 → 4I11/2, 4F3/2 → 4I13/2 respectively. Stimulated emission cross -section (σemi) and Gain bandwidth (σemi × Δλeff) were calculated. For 0.5 mol% Nd these values are found to be 3.30 × 10−20 cm2, 11 × 10−26 cm2. From the decay curve analysis the lifetime values for 4F3/2 level have been determined and these values are decreased with increase in Nd3+ ions concentration. These results may suggest that the prepared SBNCNd05 (Nd = 0.5 mol%) glass could be useful for 1056 nm laser applications.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call