Abstract
Cubic boron nitride (c-BN) films were deposited on Si substrate with poor adhesion using magnetically enhanced active reaction evaporation (ME-ARE). An attempt has been made to enhance the adhesion strength between c-BN film and substrate by nitrogen plasma based ion implantation (PBII) into c-BN film. Nitrogen ion doses range from 5×10 16 to 1×10 17 ions cm −2 at an implant voltage of 50 kV. The nitrogen ion implanted c-BN films were analyzed using FTIR, scratch test, and XPS to investigate the change of structure, adhesion strength of c-BN film, and interfacial mixing between the initial turbostratic BN (t-BN) film layer and substrate caused by nitrogen ion implantation. FTIR spectra showed little change of c-BN phase content in the films under the above implantation conditions but XPS depth elemental profile of N +-implanted boron nitride films displayed a mixed layer consisting of elements from film and substrate formed at interface. A highly optimized dynamic Monte Carlo program TAMIX was used to simulate the PBII process in a good agreement with above measured depth elemental profile. The scratch test showed that the adhesion strength evaluated in terms of the critical load of N +-implanted c-BN film was 1.4 times higher than that of as deposited c-BM film.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.