Abstract
Recently, high dosage doping on Si multi-gate field effect transistors and III–V planar structures using a self-limiting monolayer doping technique was reported to overcome challenges in scaling nano-sized transistors. The stoichiometry or composition of the capping layer was found to affect the diffusion efficiency of this process. In this work, we study the effect of a capping layer in sulfur monolayer doping on III–V junctions. Various capping temperatures and growth methods were compared. Based on the theoretical and experimental results, we suggest an optimized scheme consisting of a bi-layer capping structure. From Hall measurements and secondary ion mass spectrometry, a SiNx/BeO bi-layer capping, compared to single layer cap, exhibited the best results with a surface sheet resistance of 232 Ω/sq, junction depth of 11 nm, dopant profile abruptness of 3.5 nm/dec, electrically active S concentration of 4.9 × 1019/cm3 (=1.34 × 1013/cm2), and 3 times higher activation efficiency without significant transient-enhanced dopant diffusion.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.