Abstract
This paper highlights the interfacial structure of tin-silver (Sn-3·5Ag) solder on nickel-coated copper pads during aging performance studies at a temperature of 150°C for up to 96 h. Experimental results revealed the as-solidified solder bump made from using the lead-free solder (Sn-3·5Ag) exhibited or showed a thin layer of the tin-nickel-copper intermetallic compound (IMC) at the solder/substrate interface. This includes a sub-layer having a planar structure immediately adjacent to the Ni-coating and a blocky structure on the inside of the solder. Aging performance studies revealed the thickness of both the IMC layer and the sub-layer, having a planar structure, to increase with an increase in aging time. The observed increase was essentially non-linear. Fine microscopic cracks were observed to occur at the interfaces of the planar sub-layer and the block sub-layer.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.